TPV 201-80 埃克森美孚santoprene 热塑性elastomer

TPV 201-80颗粒图片

TPV 201-80 包装库存

TPV 201-80 物性表：

Physical Properties Metric English Comments Specific Gravity 0.960 g/cc 0.960 g/cc 23°C; ASTM D792 Mechanical Properties Metric English Comments Hardness, Shore A 86 86 2 mm, 15 sec; ISO 868 91 91 Air at 302°F, 168 hr; ASTM D573 Tensile Strength at Break 10.546 MPa 1529.5 psi Air at 302°F, 168 hr; ASTM D573 11.1 MPa 1610 psi Across Flow; ASTM D412 Tensile Stress 4.70 MPa

@Strain 100 % 682 psi

@Strain 100 % Across Flow; ASTM D412 Elongation at Break 475.2 % 475.2 % Air at 302°F, 168 hr; ASTM D573 540 % 540 % Across Flow; ASTM D412 Tear Strength 35.1 kN/m 200 pli 73°F, Die C; ASTM D624 Compression Set 41 % 41 % 158°F, 22 hr; ASTM D395 47 % 47 % 257°F, 70 hr; ASTM D395 Electrical Properties Metric English Comments Dielectric Constant 2.3 2.3 1.98 mm; ASTM D150 Dielectric Strength 32.3 kV/mm 820 kV/in 2.03 mm; ASTM D149 Thermal Properties Metric English Comments Maximum Service Temperature, Air 135 °C 275 °F Brittleness Temperature -60.0 °C -76.0 °F ASTM D746 UL RTI, Electrical 100 °C 212 °F UL 746 UL RTI, Mechanical with Impact 90.0 °C

@Thickness 1.00 mm 194 °F

@Thickness 0.0394 in UL 746 95.0 °C

@Thickness 1.50 mm 203 °F

@Thickness 0.0591 in UL 746 100 °C

@Thickness 3.00 mm 212 °F

@Thickness 0.118 in UL 746 Flammability, UL94 HB

@Thickness 1.00 mm HB

@Thickness 0.0394 in HB

@Thickness 1.50 mm HB

@Thickness 0.0591 in HB

@Thickness 3.00 mm HB

@Thickness 0.118 in Processing Properties Metric English Comments Processing Temperature 175 - 230 °C 347 - 446 °F Rear Barrel Temperature 177 °C 350 °F Middle Barrel Temperature 182 °C 360 °F Front Barrel Temperature 188 °C 370 °F Nozzle Temperature 193 - 232 °C 380 - 450 °F Die Temperature 204 °C 400 °F Extrusion Melt Temperature 202 °C 395 °F Extrusion 199 - 232 °C 390 - 450 °F Processing Mold Temperature 10.0 - 51.7 °C 50.0 - 125 °F Processing Drying Temperature 82.2 °C 180 °F Dry Time 3 hour 3 hour Moisture Content 0.080 % 0.080 % Back Pressure 0.345 - 0.689 MPa 50.0 - 100 psi Processing 5.00 - 20.0 MPa 725 - 2900 psi Extrusion Clamp Pressure 41.4 - 68.9 MPa 6000 - 10000 psi Vent Depth 0.00254 cm 0.00100 in Cushion 0.317 - 0.635 cm 0.125 - 0.250 in Screw Speed 100 - 200 rpm 100 - 200 rpm Descriptive Properties Color Natural Color Form Pellets Injection Rate Fast Maximum Regrind % 20 Screw Compression Ratio 2:1 - 2.5:1 Screw L/D Ratio 16:1 - 20:1

制品优势： 1、 优异的抗老化性能和良好的耐候、耐热性能； 2、 优异的抗永久变形性能； 3、 优异的抗张强度、高韧性和高回弹性； 4、 优异的环保性能和可重复使用； 5、 优异的电绝缘性能； 6、 硬度范围广泛； 7、 使用温度范围广泛； 8、 颜色多样化，有全透明、半透明、浅色系列，着色容易，容易加工成型； 9、 可与PP、PA、PC、ABS、PS、PBT、PET等多种材料共注射或挤出成型。 广泛应用于：电子产品外壳及外保护、建筑材料密封条、交通器材缓冲部件、消费品的主体如鱼竿牙刷吸管等、、、、、 上海松翰塑化科技有限公司与埃克森美孚长期合作供应其产品，品质一流，TPV、TPU种类齐全.咨询人褚先生 电话 QQ297262310 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询