PC/ ABS合金 MC1300 沙伯基础（原GE）汽车把手 电镀级耐冲击

性能项目试验条件[状态]测试方法测试数据数据单位物理性能吸水率24小时@73ASTM D 5700.100%平衡,0.125"ASTM D 9555-8in/in E-3熔体流动速率标称,260C/5.0 kgfASTM D 123814.0g/10min模塑收缩量xflow,0.125"ASTM D 9555-7in/in E-3比重固体ASTM D 7921.10机械性能抗伸强度屈服，类型，2.0 in/minASTM D 6387300psi挠曲模量0.05 in/min，2" spanASTM D 790300000psi抗拉强度屈服，类型I，2.0 in/minASTM D 6386400psi拉伸伸长断裂类型I，2.0 in/minASTM D 6388.6%屈服类型I，2.0 in/minASTM D 638150.0%拉伸模量2.0 in/minASTM D 638310000psi挠曲应力断裂，0.05 in/min，2" spanASTM D 79010500psi加工性能背压50-100psig含湿量（最大）0.04%合模力吨数3-5tons/psi螺杆速度40-70rpm干燥温度210-220deg F干燥时间基本3-4h最长8h温度熔体温度500-550deg F注嘴温度500-550deg F前段温度490-550deg F中段温度490-550deg F后段温度480-540deg F模具温度170-210deg F推荐注射量30-80%排气槽深度inch热性能CTE(热膨胀系数)xflow,-40F-100FASTM E 8319E-5in/in-Fflow,-40F-200FASTM E 8314E-5in/in-FHDT(热畸变温度)66 psi,0.125",未退火ASTM D 648240deg F264 psi,0.125",未退火ASTM D 648210deg F维卡软化温度B级ASTM D 1525233deg F其它性能缺口伊佐德冲击值73FASTM D 25610.0ft-lb/in-22FASTM D 2568.0ft-lb/in仪表控制抗冲击总能量73FASTM D 3763360in-lbs-22FASTM D 3763300in-lbs