ABS电瓶壳专用料 自产

牌号自产厂家(产地)自产用途级别注塑级

长期供应abs电瓶壳料物性数据数据提供企业 东莞市锦成塑胶原料有限公司性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)

ASTM D638/ISO 52744kg/cm²(MPa)[Lb/in2]断裂伸长率

ASTM D638/ISO 527

%拉伸模量

ASTM D638/ISO 527

kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率)

ASTM D638/ISO 527

%拉伸断裂伸长率(延伸率)

ASTM D638/ISO 527

%弯曲模量(弯曲弹性率)

ASTM D790/ISO 1782350kg/cm²(MPa)[Lb/in2]弯曲强度

ASTM D790/ISO 17870kg/cm²(MPa)[Lb/in2]洛氏硬度

ASTM D785R-102

IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 17911.5kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in物性性能比重（密度）

ASTM D792/ISO 11831.05

成型收缩率

ASTM D955

%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 113323.8g/10min220℃/10kgASTM D1238/ISO 1133

g/10min吸水率 23℃/24H

ASTM D570/ISO 62

%热性能热变形温度退火ASTM D648/ISO 7580℃（℉）未退火ASTM D648/ISO 75

℃（℉）维卡软化点

ASTM D1525/ISO R306

℃（℉）熔点

-

℃（℉）燃烧性（率）

UL94HB

线性膨胀系数

ASTM D696/ISO 11359

mm/mm.℃加工条件干燥条件

加工温度射嘴

205℃料筒前段

200℃料筒中段

205℃料筒后段

210℃熔体温度

℃模具温度

℃压力注塑压力

Mpa保压压力

Mpa背压

Mpa螺杆转速

rpm其他备注

颜色

特性黑色用途15|电子器材 配件 电瓶壳