PC/日本帝人/L-1250Y

产品参数性能项目试验条件[状态]测试方法测试数据数据单位吸水率24hr，in 23℃ASTM D-5700.20%透光率厚度3mmASTM D-100388%阻燃性厚度1.47mm (厚度3.05mm )UL 9494V-2比重 ASTM D-7921.20折射率 ASTM D-5421.585洛氏硬度 ASTM D-78577M标度拉伸率(屈服点)-ASTM D-6386-拉伸率(断裂点)-ASTM D-638140-弯曲模量 ASTM D-7902230(22700)Mpa(kgf/cm2)拉伸强度(屈服点)-ASTM D-63861(620)Mpa(kgf/cm2)拉伸强度(断裂点)-ASTM D-63881(830)Mpa(kgf/cm2)拉伸模量 ASTM D-6382120(21600)Mpa(kgf/cm2)弯曲强度 ASTM D-79090(915)Mpa(kgf/cm2)压缩强度 ASTM D-69576(770)Mpa(kgf/cm2)耐冲击强度值艾氏、带缺口厚度6.4mmASTM D-256140(14)j/m(kgf.cm/cm)耐冲击强度值艾氏、带缺口厚度3.2mmASTM D-256880(90)j/m(kgf.cm/cm)体积电阻率 ASTM D-25731016Ω.cm绝缘破坏强度快速加压值厚度1.6mmASTM D-14930KV/mm介电率60Hz(106Hz)ASTM D-1502.95(2.9)耐导电径迹性CTIIEC 112300V耐电弧性 ASTM D-495110secc介电正切60Hz(106Hz)ASTM D-1500.0004(0.009)成型收缩率流动方向(垂直方向)ASTM D-9550.5～0.7%线膨胀系数流动方向(垂直方向)ASTM D-696710-5cm/cm/℃负荷挠曲温度负荷0.451MPa(4.6kgf/cm)ASTM D-648143℃温度指数(电学式)厚度1.47mmUL 746B125°C温度指数(冲击式)厚度1.47mmUL 746B115°C温度指数(非冲击式)厚度1.47mmUL 746B125°C负荷挠曲温度负荷1.813MPa(18.6kgf/cm)ASTM D-648143℃

产品细节图