供应ABS台湾奇美PA-777B

通途级别：注塑级

ABS PA-777B 台湾奇美性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度) ASTM D638/ISO 527450(6,380)kg/cm2(MPa)[Lb/in2]断裂伸长率 ASTM D638/ISO 527-%拉伸模量 ASTM D638/ISO 527-kg/cm2(MPa)[Lb/in2]拉伸屈服伸长率(延伸率) ASTM D638/ISO 52715%拉伸断裂伸长率(延伸率) ASTM D638/ISO 527-%弯曲模量(弯曲弹性率) ASTM D790/ISO 17822000（31000）kg/cm2(MPa)[Lb/in2]弯曲强度 ASTM D790/ISO 178650(9,200)kg/cm2(MPa)[Lb/in2]洛氏硬度 ASTM D785R-112 IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 17920（3.7）kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 17923(4.3)kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in物性性能比重（密度） ASTM D792/ISO 11831.03 成型收缩率 ASTM D955-%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 1133-g/10min220℃/10kgASTM D1238/ISO 11337.5g/10min吸水率 23℃/24H ASTM D570/ISO 62-%热性能热变形温度退火ASTM D648/ISO 75107(225)℃（℉）未退火ASTM D648/ISO 7597(207)℃（℉）维卡软化点 ASTM D1525/ISO R306115(239)℃（℉）熔点 --℃（℉）燃烧性（率） UL941.6mmHB 线性膨胀系数 ASTM D696/ISO 11359-mm/mm.℃加工条件干燥条件 90~95°C下烘料约3小时 加工温度射嘴 220~250°C℃料筒前段 230~250 °C℃料筒中段 230~250 °℃料筒后段 220~240 °℃熔体温度 -℃模具温度 30~70°C℃压力注塑压力 50~70kg/cm2Mpa保压压力 40~60kg/cm2Mpa背压 5~15kg/cm2Mpa螺杆转速 -rpm其他备注在射出周期中勿将热融胶长期停留在加热管中颜色-特性耐热性、高冲击强度用途发热家电外壳 / 乾发吹风筒 / 熨斗外壳 / 暖风机 / 汽车零配件如仪表板 / 水箱护罩等