伊朗HDPE-EX3

HD – EX3

License Grade Code HM 5010 T2N

1) Product Description:

“EX3 (HM 5010 T2N)” is a natural colored high density polyethylene with Butene-1 as

comonomer. The product is classified as PE 80 and good stress crack resistance

properties (ESCR) combined with good impact strength.

Stabilization: Ca-Stearate, Zn-Stearate, Irganox1010, Irgafos168

2) Applications:

Pipe Extrusion PE80 Class

• Pressure pipe

• Drinking water and gas pipes

• Sewer pipes and their fittings

• Discharge pipes

• For injection moulded and other fittings

• Sheets

3) Typical DataProperty Unit TypicalValue*Test MethodMelt Flow Rate(MFR) (190 °C/2.16Kg) (190

°C/5Kg) (190 °C/21.6Kg)g/10min---0.45 12ISO 1133Density g/cm30.945ISO 1183MRS ClassificationMPa8ISO/TR9080Hydrostatic Strength(80°C ) hr1000ISO 1167 / DIN8075Tensile Modulus (23 °C, v=1mm/min),Secant MPa850ISO 527-1,2Tensile Stress @ yield (23 °C, v=50mm/min) MPa22ISO 527-1,2Tensile Strain@ yield (23 °C, v=50mm/min) %8ISO 527-1,2Tensile Creep Modulus 1h MPa ISO 899-1Tensile Stress at 3.5 % deflection MPa ISO 178Charpy Notch Impact Strength(23 °C) Kj/m212ISO 179Hardness Shore D (3 Sec) ---60ISO 868Vicat Softening Temperature °C67ISO 306Melting Point°C136ISO 3146Oxidation Induction Time (210°C) Min EN 728* Typical Values : not to be construed as specifications

4) Processing Condition:

Recommended melt temperature: 190-220 °C

Extruder for Producing Pipe: Dr.Collin E 45 M

Screw Temperature(°C): 180,200,200 Hard Temperature(°C): 200,200

Orifice Temperature(°C): 200,210 Screw speed is set to 60 to 80 rpm

The Feeder of the extruder is cooled by cooling water CWS/CWR (35-45)

Pipe Measuring: 32mm ×3mm

Licensor: Basell

Packing: 25 Kg plastic bag