中冲击强度ABS 台湾奇美 PA-757

ABS台湾奇美PA-757 物性认证数据表

性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度) ASTM D638/ISO 527490(6,950)kg/cm²(MPa)[Lb/in2]断裂伸长率 ASTM D638/ISO 527-%拉伸模量 ASTM D638/ISO 527-kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率) ASTM D638/ISO 52720%拉伸断裂伸长率(延伸率) ASTM D638/ISO 527-%弯曲模量(弯曲弹性率) ASTM D790/ISO 17827000(38000)kg/cm²(MPa)[Lb/in2]弯曲强度 ASTM D790/ISO 178790(11,660)kg/cm²(MPa)[Lb/in2]洛氏硬度 ASTM D785R-116 IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 17917(3.1)kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 17920(3.7)kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179-kg·cm/cm(J/M)ft·lb/in物性性能比重（密度） ASTM D792/ISO 11831.05 成型收缩率 ASTM D955-%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 11331.6g/10min220℃/10kgASTM D1238/ISO 113322g/10min吸水率 23℃/24H ASTM D570/ISO 62-%热性能热变形温度退火ASTM D648/ISO 7599(210)℃（℉）未退火ASTM D648/ISO 7588(190)℃（℉）维卡软化点 ASTM D1525/ISO R306105(221)℃（℉）熔点 --℃（℉）燃烧性（率） UL941.6mmHB 线性膨胀系数 ASTM D696/ISO 11359-mm/mm.℃加工条件干燥条件 80°C下烘料约2~3小时 加工温度射嘴 180~230°C℃料筒前段 190~230℃料筒中段 190~230℃料筒后段 180~220℃熔体温度 -℃模具温度 30~70°C℃压力注塑压力 -Mpa保压压力 -Mpa背压 -Mpa螺杆转速 -rpm其他备注-颜色-特性高光泽性 高刚性。用途电视机前壳 / 复印机外壳 / 电话机壳 / 化妆品盒 / 轮胎盖数据修正企业：