基础创新 AS003 抗静电ABS

Property TYPICAL PROPERTIES (1)MECHANICALValueUnitStandardTensile Stress, yield430kgf/cm²ASTM D 638Tensile Stress, break400kgf/cm²ASTM D 638Tensile Strain, yield2.2%ASTM D 638Tensile Strain, break8.6%ASTM D 638Tensile Modulus, 50 mm/min30500kgf/cm²ASTM D 638Flexural Stress770kgf/cm²ASTM D 790Flexural Modulus28700kgf/cm²ASTM D 790Tensile Stress, yield39MPaISO 527Tensile Stress, break37MPaISO 527Tensile Strain, yield2.2%ISO 527Tensile Strain, break3.3%ISO 527Tensile Modulus, 1 mm/min2500MPaISO 527Flexural Stress66MPaISO 178Flexural Modulus2500MPaISO 178IMPACTValueUnitStandardIzod Impact, unnotched, 23°C29cm-kgf/cmASTM D 4812Izod Impact, notched, 23°C5cm-kgf/cmASTM D 256Instrumented Impact Energy @ peak, 23°C121cm-kgfASTM D 3763Izod Impact, unnotched 80*10*4 +23°C20kJ/m²ISO 180/1UIzod Impact, notched 80*10*4 +23°C7kJ/m²ISO 180/1ATHERMALValueUnitStandardHDT, 0.45 MPa, 3.2 mm, unannealed97°CASTM D 648HDT, 1.82 MPa, 3.2mm, unannealed87°CASTM D 648CTE, -40°C to 40°C, flow7.92E-051/°CASTM E 831CTE, -40°C to 40°C, xflow7.56E-051/°CASTM E 831CTE, -40°C to 40°C, flow7.8E-051/°CISO 11359-2CTE, -40°C to 40°C, xflow9.6E-051/°CISO 11359-2HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm91°CISO 75/BfHDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm78°CISO 75/AfPHYSICALValueUnitStandardDensity1.12g/cm³ASTM D 792Moisture Absorption, 50% RH, 24 hrs0.2%ASTM D 570Mold Shrinkage, flow, 24 hrs (5)18%ASTM D 955Mold Shrinkage, xflow, 24 hrs (5)27%ASTM D 955Mold Shrinkage, flow, 24 hrs (5)0.18%ISO 294Mold Shrinkage, xflow, 24 hrs (5)0.27%ISO 294Density1.11g/cm³ISO 1183ELECTRICALValueUnitStandardVolume Resistivity1.E+02 - 1.E+06Ohm-cmASTM D 257Surface Resistivity1.E+01 - 1.E+05OhmASTM D 257Shielding Effectivness @ 3mm40 - 55dBSABIC Method