PC 塑胶原料日本帝人增强塑料 耐高温G-3130M BK 注塑级

产品参数性能项目试验条件[状态]测试方法测试数据数据单位吸水率24hr 23℃ASTM D-5700.12%阻燃性厚度3.05mmUL 9494V-1阻燃性厚度1.47mmUL 9494V-2比重 ASTM D-7921.43透光率厚度3mmASTM D-1003半透明%成型收缩率(流动方向) ASTM D-9550.3～0.5%成型收缩率(垂直方向) ASTM D-9550.3～0.5%压缩强度 ASTM D-69577(790)Mpa(kgf/cm2)弯曲模量 ASTM D-7903920(40000)Mpa(kgf/cm2)拉伸强度断裂点ASTM D-63856(570)Mpa(kgf/cm2)弯曲强度 ASTM D-79098(1000)Mpa(kgf/cm2)断裂伸长率 ASTM D-638>3洛氏硬度 ASTM D-78593M标度耐冲击强度值艾氏、带缺口厚度6.4mmASTM D-25650(5)j/m(kgf?cm/cm)耐冲击强度值艾氏、带缺口厚度3.2mmASTM D-25650(5)j/m(kgf?cm/cm)绝缘破坏强度快速加压值厚度1.6mmASTM D-14930KV/mm耐导电径迹性(CTI) IEC 112180V体积电阻率 ASTM D-25711016Ω.cm介电率60HzASTM D-1503.51介电正切106HzASTM D-1500.009介电正切60HzASTM D-1500.0008耐电弧性 ASTM D-495100sec介电率106HzASTM D-1503.41线膨胀系数(流动方向) ASTM D-6965.010-5cm/cm/℃线膨胀系数(垂直方向) ASTM D-6965.610-5cm/cm/℃负荷挠曲温度负荷0.451MPa(4.6kgf/cm)ASTM D-648139°C温度指数(电学式)厚度1.47mmUL 746B130°C温度指数(冲击式)厚度1.47mmUL 746B125°C温度指数(非冲击式)厚度1.47mmUL 746B130°C负荷挠曲温度负荷1.813MPa(18.6kgf/cm)ASTM D-648135°C