喷塑表面移印油墨

具有高色泽、高色彩、高遮盖力、高稳定性、耐酒精及耐磨擦之特点。

印刷：丝印移印均可。表干及实干时间：表干时间自然挥发5-10分钟；实干时间在24小时以内。稀释及清洗：SV3慢干开油水、UVK1（移印开油水）同时可使用718洗网水清洗。

测试方法（完全干燥后）：1、3m胶纸粘在画有百格的油墨表面，45度角迅速拉起不脱油;2、纯度99%的工业酒精，一千克砝码用棉布包住在油墨表面，以水平力来回拉200次无脱色; 3、耐磨：橡皮擦500g力水平来回擦500次。

使用方法： 1、使用前应充分搅拌，用后随时封闭；2、搅拌时加开油水10-15%，稀释到印刷粘度； 3、网板塞网时可用洗网水清洗； 4、不得与其它类型油墨混合使用。

注意事项：1、塑胶材料的外观相似，但可能会是不同的材料，客户需试印确定其符合要求后，再批量印刷；2、在移印过程中，如出现拉丝或散开，可适当加入一些慢干膏即可; 3、环境温度过高，将会影响油墨原有质量；4、根据气候变化，请远离火源，阴暗环境下存放。

Oles MPE Plating Ink MPE plating strengthening series ink characteristics : mainly usedin plating surface, enhanced surface, vacuum plating surface andother materials, with a high color, high color, high coveringpower, high stability, high alcohol and rub characteristics.Printing: screen printing can be. Surface drying and drying time:surface dry time natural volatile 5-10 minutes; work time within 24hours. Dilution and cleaning: SV3 slow dry open water, UVK1 (printing open water) can be simultaneously used 718 washing networkwater cleaning. Test method ( completely dry ): 1, 3M gummed paperin the paintings of the surface of the ink, 45 degree angle quicklypulled off the oil; 2, 99% of the purity of industrial alcohol, onekilogram of weight of cotton pack in the ink surface, with ahorizontal force pulling back and forth 200 times withoutdecolorization; 3: oak, wear resistance eraser 500g force levelbrush back and forth 500 times. Usage: 1, use should be fullystirred, use at any time after the closure; 2, add water mixing10-15%, diluted to 3, screen printing viscosity; the plug isavailable when washing network water cleaning; 4, not with othertypes of ink mixing. Note: 1, the plastic material similar inappearance, but may be of different materials, customers need totry to determine its requirements, and then batch printing; 2, inthe printing process, such as drawing or spread out, may beappropriate to add some slow dry plaster; 3, the ambienttemperature is too high, will affect the quality of the originalink; 4, according to climate change, please stay away from fire,dark environment storage.