供应原装乐泰环氧树脂胶粘剂 11C

LOCTITE®Hysol®11C™ is a general purpose adhesive andsealant that bonds, seals, and repairs a wide variety of

materials including metals, most plastics, and wood.

TYPICAL PROPERTIES OF UNCURED MATERIAL

Resin:

Specific Gravity @ 25 °C 1.6

Flash Point - See MSDS

Viscosity, Brookfield - RV, 25 °C, mPa·s (cP):

Spindle 7, speed 10 rpm 140,000 to 330,000

Hardener:

Specific Gravity @ 25 °C 1.67

Flash Point - See MSDS

Viscosity, Brookfield - RV, 25 °C, mPa·s (cP):

Spindle 7, speed 2 rpm 500,000 to 900,000

Mixed:

Pot life 100 grams, @ 25 °C, minutes ≥20LMS

TYPICAL PROPERTIES OF CURED MATERIAL

Cured for 1 hour @ 90 °C

Outgassing Properties:

Total Mass Loss, % 0.47

Collected Volatile Condensable Material, % 0.02

Cured for 2 hours @ 60 °C

Physical Properties:

Shore Hardness, ISO 868, Durometer D ≥65

LMS

Cured for 3 hours @ 120 °C

Physical Properties:

Glass Transition Temperature (Tg) by DSC, °C 114

Cured for 3 days@ 25 °C, tested @ 100 °C

Physical Properties:

Coefficient of Thermal Conductivity, ASTM E 1530,

W/(m·K)

0.75

Cured for 3 days @ 25 °C

Physical Properties:

Coefficient of Thermal Expansion,

ISO 11359-2, K

-1

:

Pre Tg 38×10

-6

Post Tg 134×10

-6

Electrical Properties:

Dielectric Breakdown Strength,

IEC 60243-1, kV/mm

18.5

Dielectric Constant / Dissipation Factor, IEC 60250:

1-kHz 5.0 / 0.05

Volume Resistivity, IEC 60093, Ω·cm 5.0×10

14

Surface Resistivity, IEC 60093, , Ω ≥9.47×10

16

TYPICAL PERFORMANCE OF CURED MATERIAL

Adhesive Properties

Cured for 3 days @ 25 °C

Lap Shear Strength, ISO 4587:

Aluminum (etched):

Tested @ -55 °C N/mm² 7.8

(psi) (1,130)

Tested @ 25 °C N/mm² 16.5

(psi) (2,390)

Tested @ 82 °C N/mm² 15.6

(psi) (2,270)

Tested @ 121 °C N/mm² 10.5

(psi) (1,520)

Tested @ 149 °C N/mm² 4.1

(psi) (600)