泰国普力迈ABS POLIMAXX KU650

ABS POLIMAXX GA850General

Material Status Commercial: ActiveAvailability Asia PacificEuropeNorth AmericaFeatures Food Contact AcceptableGeneral PurposeHigh Impact ResistanceUses Appliance ComponentsElectrical/Electronic ApplicationsGeneral PurposeHousehold GoodsToysAgency Ratings

RoHS Compliance Processing Method Injection MoldingPhysicalNominal ValueUnitTest MethodMelt Mass-Flow Rate (MFR) (220°C/10.0 kg)

g/10 minASTM D1238MechanicalNominal ValueUnitTest MethodTensile Strength (Yield, 73°F)

psiASTM D638Flexural Modulus (73°F)

psiASTM D790Flexural Strength (Yield, 73°F)

psiASTM D790ImpactNominal ValueUnitTest MethodNotched Izod Impact (73°F, 0.250 in)

ft·lb/inASTM D256HardnessNominal ValueUnitTest MethodRockwell Hardness (R-Scale, 73°F, 0.250 in)

ASTM D785ABS POLIMAXX GA850 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！成型性能

无定形材料,流动性中等,吸湿大,必须充分干燥,表面要求光泽的塑件须长时间预热干燥80-90度,3小时；

宜取高料温,高模温,但料温过高易分解(分解温度为>270度).对精度较高的塑件,模温宜取50-60度,对高光泽.耐热塑件,模温宜取60-80度；

如需解决夹水纹，需提高材料的流动性，采取高料温、高模温，或者改变入水位等方法；

如成形耐热级或阻燃级材料，生产3-7天后模具表面会残存塑料分解物，导致模具表面发亮，需对模具及时进行清理，同时模具表面需增加排气位置；

冷却速度快，模具浇注系统应以粗，短为原则，宜设冷料穴，浇口宜取大，如：直接浇口，圆盘浇口或扇形浇口等，但应防止内应力增大，必要时可采用调整式浇口。模具宜加热，应选用耐磨钢；

料温对塑件质量影响较大，料温过低会造成缺料，表面无光泽，银丝紊乱料温过高易溢边，出现银丝暗条，塑件变色起泡；

用途

ABS树脂的最大应用领域是汽车、电子电器和建材。汽车领域的使用包括汽车仪表板、车身外板、内装饰板、方向盘、隔音板、门锁、保险杠、通风管等很多部件。在电器方面则广泛应用于电冰箱、电视机、洗衣机、空调器、计算机、复印机等电子电器中。建材方面，ABS管材、ABS卫生洁具、ABS装饰板广泛应用于建材工业。此外ABS还广泛的应用于包装、家具、体育和娱乐用品、机械和仪表工业中。