牌号 |
LD7650 |
品牌/厂家 |
韩国LG |
产地 |
韩国LG |
熔体流动速率 |
7.0g/10min |
密度 |
1.2g/cm3 |
拉伸强度 |
61.8kg/cm2 |
弯曲强度 |
98.1kg/cm2 |
长茂塑胶供应:
PC LG LD7650
PC LG LD7650I
PC LG LD7700
PC LG LD7701F
PC LG LD7701FD
PC LG LD7750
PC LG LD7800
PC LG LD7850
PC LG LD7890
PC LG LD7890H
LUPOY PC 1200-08
LUPOY PC 1200-10
LUPOY PC 1200-22
LUPOY PC 1201-08
LUPOY PC 1201-10
LUPOY PC 1201-15
LUPOY PC 1201-18
LUPOY PC 1201-22
LUPOY PC 1300-03
LUPOY PC 1300-10
LUPOY PC 1300-15
LUPOY PC 1300-22
LUPOY PC 1300-30
LUPOY PC 1301-12
LUPOY PC 1301-22
LUPOY PC 1301EP-30
LUPOY PC 1302-05
LUPOY PC 1302-07
LUPOY PC 1302-10
LUPOY PC 1302UV-08
LUPOY PC 1303-07
LUPOY PC 1303-10C
LUPOY PC 1303-15
LUPOY PC 1303AH-10
LUPOY PC 1303AH-15
LUPOY PC 1303EP-22
LUPOY PC 1301V-10
LUPOY PC 1080-70
LUPOY PC 1261-03
LUPOY PC 1600-03
LUPOY PC 1603-03
LUPOY PC 1603-06
LUPOY PC 1621-02
LUPOY PC 1200HP-15
LUPOY PC 1201HP-08
LUPOY PC 1302HP-07
LUPOY PC 1302HP-09
LUPOY PC 1302HP-10
LUPOY PC 1302HP-21
LUPOY PC 1302HP-22
LUPOY PC 3010-10
LUPOY PC 3010-15
LUPOY PC 3010-30
LUPOY PC 3030-08
LUPOY PC 3030-10
LUPOY PC 3030-15
LUPOY PC NF1005F-03R
LUPOY PC NF1007F-10R
LUPOY PC NF1009F-08R
LUPOY PC NF1009F-15
LUPOY PC 1320C-07
PC聚碳酸酯塑胶材料成型过程中产生的缺陷和解决办法在对PC聚碳酸酯塑胶材料进行成型加工的过程中,会出现许多的表面缺陷,主要表现为银丝或者气泡,以及树脂变色其黑点,还有所制得的制品为充满,收缩出现阵空泡,还有其透明度有所降低以及出现熔接痕和制品发生开裂,在脱模时比较困难,发生翘曲现象和溢边等不足之处,以下做单一的介绍,以及说明解决其不足缺陷的方法。
❶:银丝缺陷原因解决方法A、在加工成型之前原材料受潮 A、在成型前对原料进行干燥处理B、成型时树脂材料过热产生分解 B、成型过程中适当减低成型温度C、螺杆压缩比小,背压不足 C、增加背压D、模具的温度不够高 D、对模具进行加热E、排气排的不够好 E、模具分型面开设排气槽
❷:气泡缺陷原因解决方法A、在加工成型之前原材料受潮 A、在成型前对原料进行干燥处理B、排气排的不够好 B、对模具进行改进
❸树脂变色起黑点缺陷原因解决方法A、料筒或者喷嘴积了料 A、对料筒或者喷嘴进行清理B、成型温度过高 B、降低成型温度
❹制品未充满缺陷原因解决方法A、物料塑化的不够 A、提高料筒的温度B、喷嘴溢料 B、调整模具的位置C、注射压力过低 C、提高注射压力D、加料量过少 D、调整加料量
❺收缩真空气泡缺陷原因解决方法A、保压不足 A、延长保压的时间B、注射压力过低 B、提高注射压力C、模具设计不合理 C、增加流道和浇口的尺寸
❻透明度降低缺陷原因解决方法A、原材料受潮 A、干燥原料B、模具温度过低 B、提高模具温度C、物料过热分解 C、降低成型温度