日本旭化成PA66 1200S,1300S

产品参数性能项目试验条件[状态]测试方法测试数据数据单位吸湿率湿2.5%比重乾ASTM D7921.14成型收缩率，3mm厚，平行/垂直于流动方向乾旭化成1.3-2.0%(断裂)延伸率乾ASTM D63850%洛氏硬度湿ASTM D78555/108M/RIZOD冲击强度(带缺口)湿ASTM D25614kgf.cm/cmIZOD冲击强度(带缺口)乾ASTM D2563.5kgf.cm/cm弯曲模量湿ASTM D79012 000kgf/cm2洛氏硬度乾ASTM D78580/120M/R弯曲强度湿ASTM D790550kgf/cm2弯曲模量乾ASTM D79028 550kgf/cm2拉伸强度乾ASTM D638780kgf/cm2弯曲强度乾ASTM D7901200kgf/cm2(断裂)延伸率湿ASTM D638250%Taber磨耗率湿ASTM D10447mg/1000次拉伸强度湿ASTM D638530kgf/cm2热变形温度乾ASTM D64870°C 18.2kgf/cm2线性膨胀系数乾ASTM D69681e-5/cm.°C热变形温度乾ASTM D648230°C 0.46kgf/cm2阻燃性DryUL 94V-2