PC K-1300

产品参数性能项目试验条件[状态]测试方法测试数据数据单位比重 ASTM D-7921.20成型收缩率流动方向ASTM D-9550.5~0.7%透光率厚度3mmASTM D-100389%折射率 ASTM D-5421.585吸水率23°C水中24小时ASTM D-5700.20%成型收缩率垂直方向ASTM D-9550.5~0.7%耐冲击强度值艾氏、带缺口厚度3.2mmASTM D-256930(95)j/m(kgf?cm/cm)拉伸模量 ASTM D-6382090(21300)Mpa(kgf/cm2)负荷-挠曲温度负荷0.451MPa(4.6kgf/cm)ASTM D-648146℃耐冲击强度值艾氏、带缺口厚度6.4mmASTM D-256160(16)j/m(kgf?cm/cm)压缩强度 ASTM D-69575(760)Mpa(kgf/cm2)负荷-挠曲温度负荷-挠曲温度ASTM D-648136℃拉伸率(屈服) ASTM D-6386拉伸率(断裂) ASTM D-638130弯曲模量 ASTM D-7902190(22300)Mpa(kgf/cm2)拉伸强度(屈服) ASTM D-63860(610)Mpa(kgf/cm2)拉伸强度(断裂) ASTM D-63884(860)Mpa(kgf/cm2)洛氏硬度M标度ASTM D-78577弯曲强度 ASTM D-79087(890)Mpa(kgf/cm2)阻燃性厚度1.47mmUL 9494V-2介电率 ASTM D-1500.009106Hz阻燃性厚度3.05mmUL 9494V-2耐电弧性 ASTM D-495110sec介电率60HzASTM D-1502.95体积电阻率 ASTM D-2573×1016Ω.cm耐导电径迹性(CTI IEC 112300V绝缘破坏强度快速加压值厚度1.6mmASTM D-14930KV/mm温度指数(电学式)厚度1.47mmUL 746B125℃温度指数(冲击式)厚度1.47mmUL 746B115℃温度指数(非冲击式)厚度1.47mmUL 746B125℃线膨胀系数流动方向ASTM D-6967×10-5cm/cm/℃线膨胀系数垂直方向ASTM D-6967×10-5cm/cm/℃