专业 低摩擦 中低粘度 赛钢料 POM 韩国工程 F25-63 聚甲醛

产品参数性能项目试验条件[状态]测试方法测试数据数据单位基本性能比重ASTM D792, ISO 11831.41g/cm3;熔体质量流动速率ASTM D1238, ISO 113315g/10 min成型收缩率flow,3.00MMASTM D9552.0%成型收缩率3.00mmISO 294-42.0%吸水率Equilibrium,23℃,60%rhASTM D5700.22%洛氏硬度M-ScaleASTM D78580机械性能拉伸强度Yield,23℃ASTM D63859.0MPa拉伸强度Yield,23℃ISO 527-263.0MPa拉伸伸长率Break,23℃ISO 527-232%拉伸伸长率Break,23℃ASTM D63850%弯曲模量23°CASTM D7902400MPa弯曲强度23°CASTM D79081.0MPa弯曲模量23°CISO 1782500MPa弯曲强度23°CISO 17885.0MPa夏比缺口冲击强度ISO 179/1eA6.0kJ/m2;Izod缺口冲击强度3.20mmASTM D25659.0J/m电气性能表面电阻率ASTM D2571.0E+11ohms表面电阻率IEC 600931.0E+12ohms体积电阻率IEC 600931.0E+11ohm·cm体积电阻率ASTM D2571.0E+10ohm·cm电气强度IEC 60243-119kV/mm热性能热畸变温度0.45MPa,未退火ASTM D648158°C热畸变温度1.8MPa,未退火ISO 75-2/A95.0°C熔融温度ASTM D3418165°C线性热膨胀系数flow,20 to 80°CASTM D6960.00013cm/cm/°C其它性能阻燃等级0.8mmUL 94HB