PC-日本帝人-G3110M

产品参数性能项目试验条件[状态]测试方法测试数据数据单位吸水率24hr 23℃ASTM D-5700.16%阻燃性厚度3.05mmUL 9494V-0比重 ASTM D-7921.27阻燃性厚度1.47mmUL 9494V-2透光率厚度3mmASTM D-1003半透明%断裂伸长率 ASTM D-638>15洛氏硬度 ASTM D-78586M标度拉伸模量 ASTM D-6382650(27000)Mpa(kgf/cm2)耐冲击强度值艾氏、带缺口厚度6.4mmASTM D-25680(8)j/m(kgf?cm/cm)弯曲模量 ASTM D-7902550(26000)Mpa(kgf/cm2)耐冲击强度值艾氏、带缺口厚度3.2mmASTM D-25680(8)j/m(kgf?cm/cm)压缩强度 ASTM D-69576(780)Mpa(kgf/cm2)弯曲强度 ASTM D-79091(930)Mpa(kgf/cm2)拉伸强度断裂点ASTM D-63858(590)Mpa(kgf/cm2)绝缘破坏强度快速加压值厚度1.6mmASTM D-14930KV/mm耐导电径迹性(CTI) IEC 112180V耐电弧性 ASTM D-495100sec体积电阻率 ASTM D-25711016Ω.cm介电正切60HzASTM D-1500.0008介电正切106HzASTM D-1500.009介电率60HzASTM D-1503.16介电率106HzASTM D-1503.07成型收缩率(流动方向) ASTM D-9550.5～0.7%成型收缩率(垂直方向) ASTM D-9550.5～0.7%负荷挠曲温度负荷1.813MPa(18.6kgf/cm)ASTM D-648133°C线膨胀系数(流动方向) ASTM D-9557.010-5cm/cm/°c线膨胀系数(垂直方向) ASTM D-9557.410-5cm/cm/°c温度指数(电学式)厚度1.47mmUL 746B130°C温度指数(冲击式)厚度1.47mmUL 746B120°C温度指数(非冲击式)厚度1.47mmUL 746B130°C负荷挠曲温度负荷0.451MPa(4.6kgf/cm)ASTM D-648137°C