牌号 |
505R |
品牌/厂家 |
基础创新塑料美国 |
产地 |
沙伯基础 |
熔体流动速率 |
10.5g/10min |
密度 |
1.20g/cm3 |
拉伸强度 |
546kg/cm2 |
弯曲强度 |
93.1kg/cm2 |
弯曲模量 |
2340kg/cm2 |
缺口冲击强度 |
800kg.cm/cm |
断裂伸长率 |
7/0% |
成型收缩率 |
0.50-0.70% |
热变形温度 |
138℃ |
脆化温度 |
154℃ |
维卡软化点 |
280°F |
沙伯基础创新PC Lexan PC 505R 10% GR . Optimum combination of high modulus plus excellent impact strength and flame retardance. UV-stabilized. Internal mold release.
SABIC Innovative Plastics Lexan® 505R PCCategories:Polymer; Thermoplastic; Polycarbonate (PC)
Material Notes:Lexan* 505R Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. Lexan 505R contains non-chlorinated, non-brominated flame retardant systems with UL-94 V0 rating at 1.5mm. It is available in various opaque color options for high stiffness applications.
Vendors:No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.
Add to Folder: My Folder Physical PropertiesMetricEnglishCommentsSpecific Gravity 1.26 g/cc1.26 g/ccASTM D792Density 1.25 g/cc0.0452 lb/in³ISO 1183Moisture Absorption 0.130 %0.130 %23°C / 50% RH; ISO 62Water Absorption at Saturation 0.31 %0.31 %ISO 62Linear Mold Shrinkage, Flow 0.0020 - 0.0060 cm/cm0.0020 - 0.0060 in/inon Tensile Bar; SABIC Method 0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm0.0050 - 0.0070 in/in
@Thickness 0.126 inSABIC MethodMelt Flow 7.0 g/10 min
@Load 1.20 kg,
Temperature 300 °C7.0 g/10 min
@Load 2.65 lb,
Temperature 572 °FASTM D1238Melt Index of Compound 7.0 g/10 min
@Load 1.20 kg,
Temperature 300 °C7.0 g/10 min
@Load 2.65 lb,
Temperature 572 °FMVR [cm^3/10 min]; ISO 1133 Mechanical PropertiesMetricEnglishCommentsHardness, H358/30 115 MPa16700 psiISO 2039-1Tensile Strength at Break 45.0 MPa6530 psi5 mm/min; ISO 527 48.0 MPa6960 psiType I, 5 mm/min; ASTM D638Tensile Strength, Yield 60.0 MPa8700 psi5 mm/min; ISO 527 63.0 MPa9140 psiType I, 5 mm/min; ASTM D638Elongation at Break 7.0 %7.0 %5 mm/min; ISO 527 12 %12 %Type I, 5 mm/min; ASTM D638Elongation at Yield 3.0 %3.0 %Type I, 5 mm/min; ASTM D638 5.0 %5.0 %5 mm/min; ISO 527Tensile Modulus 3.30 GPa479 ksi1 mm/min; ISO 527 3.93 GPa570 ksi5 mm/min; ASTM D638Flexural Strength 108 MPa15700 psibrk, 1.3 mm/min, 50 mm span; ASTM D790Flexural Yield Strength 95.0 MPa13800 psi2 mm/min; ISO 178Flexural Modulus 3.40 GPa493 ksi2 mm/min; ISO 178 3.53 GPa512 ksi1.3 mm/min, 50 mm span; ASTM D790Izod Impact, Notched 1.07 J/cm2.00 ft-lb/inASTM D256 0.800 J/cm
@Temperature -30.0 °C1.50 ft-lb/in
@Temperature -22.0 °FASTM D256Izod Impact, Unnotched 16.02 J/cm30.01 ft-lb/inASTM D4812Izod Impact, Notched (ISO) 8.00 kJ/m²3.81 ft-lb/in²80*10*4; ISO 180/1A 10.0 kJ/m²4.76 ft-lb/in²80*10*3; ISO 180/1A 8.00 kJ/m²
@Temperature -30.0 °C3.81 ft-lb/in²
@Temperature -22.0 °F80*10*3; ISO 180/1A 8.00 kJ/m²
@Temperature -30.0 °C3.81 ft-lb/in²
@Temperature -22.0 °F80*10*4; ISO 180/1AIzod Impact, Unnotched (ISO) NBNB80*10*3; ISO 180/1U NBNB80*10*4; ISO 180/1U 130 kJ/m²
@Temperature -30.0 °C61.9 ft-lb/in²
@Temperature -22.0 °F80*10*3; ISO 180/1U NB
@Temperature -30.0 °CNB
@Temperature -22.0 °F80*10*4; ISO 180/1UCharpy Impact Unnotched NBNBEdgew 80*10*4 sp=62mm; ISO 179/1eU NBNBEdgew 80*10*3 sp=62mm; ISO 179/1eU NB
@Temperature -30.0 °CNB
@Temperature -22.0 °FEdgew 80*10*3 sp=62mm; ISO 179/1eU NB
@Temperature -30.0 °CNB
@Temperature -22.0 °FEdgew 80*10*4 sp=62mm; ISO 179/1eUCharpy Impact, Notched 0.900 J/cm²4.28 ft-lb/in²Edgew 80*10*4 sp=62mm; ISO 179/1eA 1.00 J/cm²4.76 ft-lb/in²Edgew 80*10*3 sp=62mm; ISO 179/1eA 1.50 J/cm²7.14 ft-lb/in²ISO 179/2C 0.900 J/cm²
@Temperature -30.0 °C4.28 ft-lb/in²
@Temperature -22.0 °FEdgew 80*10*3 sp=62mm; ISO 179/1eADart Drop, Total Energy 61.0 J
@Temperature 23.0 °C45.0 ft-lb
@Temperature 73.4 °FASTM D3763Taber Abrasion, mg/1000 Cycles 1111CS-17, 1 kg; SABIC Method Electrical PropertiesMetricEnglishCommentsVolume Resistivity >= 1.00e+15 ohm-cm>= 1.00e+15 ohm-cmIEC 60093Surface Resistance >= 1.00e+15 ohm>= 1.00e+15 ohmROA; IEC 60093Dielectric Constant 2.8
@Frequency 1.00e+6 Hz2.8
@Frequency 1.00e+6 HzIEC 60250 2.9
@Frequency 50.0 - 60.0 Hz2.9
@Frequency 50.0 - 60.0 HzIEC 60250Dielectric Strength 16.0 kV/mm
@Thickness 3.20 mm406 kV/in
@Thickness 0.126 inin oil; IEC 60243-1 25.0 kV/mm
@Thickness 1.60 mm635 kV/in
@Thickness 0.0630 inin oil; IEC 60243-1 33.0 kV/mm
@Thickness 0.800 mm838 kV/in
@Thickness 0.0315 inin oil; IEC 60243-1Dissipation Factor 0.0010
@Frequency 50.0 - 60.0 Hz0.0010
@Frequency 50.0 - 60.0 HzIEC 60250 0.010
@Frequency 1.00e+6 Hz0.010
@Frequency 1.00e+6 HzIEC 60250Comparative Tracking Index 150 V150 VIEC 60112 Thermal PropertiesMetricEnglishCommentsCTE, linear, Parallel to Flow 40.0 µm/m-°C
@Temperature 23.0 - 80.0 °C22.2 µin/in-°F
@Temperature 73.4 - 176 °FISO 11359-2 46.8 µm/m-°C
@Temperature -40.0 - 40.0 °C26.0 µin/in-°F
@Temperature -40.0 - 104 °FASTM E 831CTE, linear, Transverse to Flow 70.0 µm/m-°C
@Temperature 23.0 - 80.0 °C38.9 µin/in-°F
@Temperature 73.4 - 176 °FISO 11359-2 84.6 µm/m-°C
@Temperature -40.0 - 40.0 °C47.0 µin/in-°F
@Temperature -40.0 - 104 °FASTM E 831Thermal Conductivity 0.210 W/m-K1.46 BTU-in/hr-ft²-°FISO 8302Deflection Temperature at 0.46 MPa (66 psi) 144 °C291 °FEdgew 120*10*4 sp=100mm; ISO 75/Be 143 °C
@Thickness 3.20 mm289 °F
@Thickness 0.126 inunannealed; ASTM D648Deflection Temperature at 1.8 MPa (264 psi) 136 °C277 °FEdgew 120*10*4 sp=100mm; ISO 75/Ae 136 °C277 °FAnnealed 120°C, 2hrs; ISO 75/Ae 138 °C
@Thickness 3.20 mm280 °F
@Thickness 0.126 inunannealed; ASTM D648Vicat Softening Point 141 °C286 °FRate B/50; ISO 306 143 °C289 °FRate B/120; ISO 306 149 °C300 °FRate B/50; ASTM D1525UL RTI, Electrical 130 °C266 °FUL 746BUL RTI, Mechanical with Impact 130 °C266 °FUL 746BUL RTI, Mechanical without Impact 130 °C266 °FUL 746BFlammability, UL94 V-0
@Thickness 1.50 mmV-0
@Thickness 0.0591 inUL 94 5VA
@Thickness 3.00 mm5VA
@Thickness 0.118 inUL 94Oxygen Index 37 %37 %ISO 4589Glow Wire Test 825 °C1520 °FIEC 60695-2-13 960 °C
@Thickness 1.00 mm1760 °F
@Thickness 0.0394 inIEC 60695-2-12 Descriptive PropertiesBall Pressure Test, 125°C +/- 2°CPASSESIEC 60695-10-2
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb's terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
Celanese Vectra® L130 Liquid Crystal Polymer (LCP), 30% Glass Reinforced
SABIC Innovative Plastics Lexan® 121 PC
SABIC Innovative Plastics Lexan® 925 PC
SABIC Innovative Plastics ULTEM 1000 PEI
Advanced Polymer Alloys DuraGrip™ 6160 BK Melt Processable Elastomer