长期供应 PA66 德国巴斯夫 A3EG6 30%玻纤增强

性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度) ASTM D638/ISO 52710000/7200kg/cm²(MPa)[Lb/in2]断裂伸长率 ASTM D638/ISO 5273/5%拉伸模量 ASTM D638/ISO 527 kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率) ASTM D638/ISO 527 %拉伸断裂伸长率(延伸率) ASTM D638/ISO 527 %弯曲模量(弯曲弹性率) ASTM D790/ISO 1788600/7000kg·cm/cm(J/M)ft·lb/in弯曲强度 ASTM D790/ISO 178280/220kg·cm/cm(J/M)ft·lb/in洛氏硬度 ASTM D785 IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 17913/22kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 17911kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179 kg·cm/cm(J/M)ft·lb/in物性性能比重（密度） ASTM D792/ISO 11831.36 成型收缩率 ASTM D955 %熔融指数（流动系数）200℃/5kgASTM D1238/ISO 113340g/10min220℃/10kgASTM D1238/ISO 1133 g/10min吸水率 23℃/24H ASTM D570/ISO 625.2-5.8%热性能热变形温度退火ASTM D648/ISO 75250 1.8Mpa℃（℉）未退火ASTM D648/ISO 75 ℃（℉）维卡软化点 ASTM D1525/ISO R306 ℃（℉）熔点 -260℃（℉）燃烧性（率） UL9494HB 线性膨胀系数 ASTM D696/ISO 113591.5-2/6-7mm/mm.℃电气性能介电常数100HZASTM D150/IEC 602503.6/5.6 1MHZASTM D150/IEC 60250 体积电阻率 ASTM D257/IEC 6009310^15/10^12Ω.cm表面电阻率 ASTM D257/IEC 6009310^12/10^10Ω耐电弧性 ASTM D495/IEC 60112 加工条件干燥条件 加工温度射嘴 ℃料筒前段 ℃料筒中段 ℃料筒后段 ℃熔体温度 ℃模具温度 ℃压力注塑压力 Mpa保压压力 Mpa背压 Mpa螺杆转速 rpm其他备注 颜色 特性玻纤增强注射级，用于需要高刚性和尺寸稳定性的机械部件护罩，插座外罩，冷却风扇，汽车冷却系统水室以及电绝缘制品用途